NEOFLON™ AP-201
全氟烷氧基
DAIKIN AMERICA, INC.

产品说明

NEOFLON PFA is a copolymer of tetrafluoroethylene and perfluoroalkyl vinyl ether, NEOFLON PFA is a compound of carbon atoms and fluorine atoms in which a perfluoroalkoxy radical is bonded to the carbon chain in the following molecular structure.

NEOFLON PFA has better mechanical strength at high temperatures than NEOFLON FEP, and has excellent moldability for easy of processing by extrusion, compression, blow, transfer, and injection molding methods. Due to the high bonding strength of the carbon, fluorine and oxygen atoms, NEOFLON PFA demonstrates nearly the same outstanding capabilities as PTFE in temperatures ranging -200°C ~+260°C. NEOFLON PFA has excellent transparency for use in melt-flow processing.

总体    
材料状态 • 已商用：当前有效   
供货地区 • 北美洲   
 • Good Corrosion Resistance • 良好的成型性能 • 清晰度，高 
性能特点 • 低摩擦系数 • 良好的电气性能  
 • 高温强度 • 流动性高 • 阻燃性能 
    
 • 共聚物 • 耐气候影响性能良好  
用途 • 薄壁部件 • 电线护套  
外观 • 半透明 • 可用颜色  
形式 • 颗粒料   
加工方法 • 挤出 • 注射成型  

物理性能  额定值单位制 测试方法
比重 2.14 到 2.16g/cm³ ASTM D792
表观密度 1.00 到 1.40g/cm³ JIS K6891
熔流率 (372°C/5.0 kg) 20 到 30g/10 min ASTM D1238
吸水率 (饱和)  < 0.010% ASTM D570
机械性能  额定值单位制 测试方法
抗张强度 (屈服) 24.5 到 29.4MPa JIS K6891
伸长率 (断裂) 350 到 450% JIS K6891
弯曲模量 580 到 690MPa ASTM D790
压缩模量 490 到 590MPa ASTM D695
压缩强度   ASTM D695
1% 应变 4.90 到 5.90MPa 
25% 应变 31.4 到 33.3MPa 
摩擦系数 (与钢 - 静态) 0.040 到 0.050 
负载变形   ASTM D621
25°C, 14 MPa 2 8.00 到 9.00% 
25°C, 14 MPa 3 2.50 到 3.00% 
100°C, 6.9 MPa 2 8.50 到 9.50% 
100°C, 6.9 MPa 3 2.00 到 3.00% 
Flexural Strength No break ASTM D790
冲击性能  额定值单位制 测试方法
悬壁梁缺口冲击强度  无断裂 ASTM D256
硬度  额定值单位制 测试方法
硬度计硬度 (邵氏 D) 60 到 70 ASTM D2240
热性能  额定值单位制 测试方法
熔融温度 300 到 310°C ASTM D4591
线形膨胀系数 - 流动 (20 到 100°C) 0.00012cm/cm/°C ASTM D696
比热  1050J/kg/°C 
导热系数  0.26W/m/K ASTM C177
可燃性  额定值单位制 测试方法
UL 阻燃等级 (1.57 mm)  V-0 UL 94
极限氧指数 (1.57 mm)  > 95% ASTM D2863
充模分析  额定值单位制 
熔体粘度 (380°C) 2.00E+6 到 2.50E+7mPa•s